干燥剂对中空玻璃的腐蚀分析
于方永1，解玉姣1
1.山东理工大学,淄博 255000
摘要：本文针对腐蚀失效的中空玻璃进行宏观和微观分析，并对中空玻璃用干燥剂的组成成分、掺杂剂含量及其对中空玻璃的腐蚀影响进行研究，最终得出干燥剂中氯化钙的掺杂、潮湿环境是造成中空玻璃腐蚀失效的主要原因，并据此提出了合理的改进建议和解决方案。
关键词：中空玻璃用干燥剂；中空玻璃寿命；腐蚀；氯化钙；潮湿环境
Corrosion analysis of insulating glass caused by desiccant
YU Fangyong1, XIE yujiao1
（1. Shandong University of Technology, Zibo 255000）
Abstract: In this paper, the reason for the corrosion failure of insulating glass were studied by macro and micro analysis. Moreover, the composition and dopant content of the desiccant, which was used for insulating glass, were investigated to find out the corrosion effect on insulating glass. On the basis of the experimental results, the doping of calcium chloride into desiccant and the humid environment were the main causes for the corrosion failure of insulating glass. Finally, some reasonable suggestions and solution were also proposed.
Key words: insulating glass desiccant; insulating glass lifespan; corrosive; calcium chloride; humid environment
引言
作为材料和生产工艺均很成熟的玻璃制品，中空玻璃因其较长的使用寿命、优良的保温、隔热和隔音等性能，被建筑工程广泛应用[1, 2]。实际应用过程中，为了提高中空玻璃的使用寿命和性能，通常需要采用能够持续控制低温露点的干燥剂[3-6]。但是，中空玻璃会因使用含有氯化钙的干燥剂而内部腐蚀结碱，最终造成失效，出现起雾、结露等现象，严重的甚至会出现玻璃坠落[7, 8]。为了避免中空玻璃内部腐蚀问题的出现，本文系统研究和分析了其腐蚀成因，并为中空玻璃的腐蚀与防护提出了建议和解决方案。
1. 实验过程
1.1 实验材料及仪器设备
实验材料：本文采用的中空玻璃样品是北方某业主单位提供的发生腐蚀失效的硅酮胶密封槽铝式双道密封建筑（安全）中空玻璃，该中空玻璃采用的铝间隔条，铝间隔条内灌装了中空玻璃用B类干燥剂，又通过第一道丁基热熔密封胶和第二道硅酮密封胶将两片玻璃粘接密封在一起。使用腐蚀失效的中空玻璃的门窗是既有住宅门窗，使用时间为7年左右。其它实验材料包括：铝间隔条试片，中空玻璃用干燥剂，氯化钙（分析纯），去离子水，盐酸溶液（1+3），三乙醇胺溶液（1+2），氢氧化钠溶液（100 g/L），钙试剂羧酸钠盐指示剂，乙二胺四乙酸二钠标准溶液（0.05 mol/L）。
实验设备：针对严重腐蚀的中空玻璃及其中的干燥剂，本文采用了宏观观察、化学成分分析、微观结构表征和腐蚀速率计算等方法进行研究，采用的实验设备主要包括：扫描式电子显微镜-能谱仪(Carl Zeiss SMT AG，德国)，X射线衍射仪(Cu-Ka 射线，35 kV，30 mA，l = 0.15418 nm)，X射线荧光光谱分析(ZSX-100e，日本)，分析天平，搅拌器，烧杯，玻璃棒，容量瓶，移液管，锥形瓶，滤纸。
山东省威海银滩中房蔚然海岸小区-含有氯化钙干燥剂对中空玻璃的腐蚀实拍
于方永1，解玉姣1
1.山东理工大学,淄博 255000
摘要：本文针对腐蚀失效的中空玻璃进行宏观和微观分析，并对中空玻璃用干燥剂的组成成分、掺杂剂含量及其对中空玻璃的腐蚀影响进行研究，最终得出干燥剂中氯化钙的掺杂、潮湿环境是造成中空玻璃腐蚀失效的主要原因，并据此提出了合理的改进建议和解决方案。
关键词：中空玻璃用干燥剂；中空玻璃寿命；腐蚀；氯化钙；潮湿环境
Corrosion analysis of insulating glass caused by desiccant
YU Fangyong1, XIE yujiao1
（1. Shandong University of Technology, Zibo 255000）
Abstract: In this paper, the reason for the corrosion failure of insulating glass were studied by macro and micro analysis. Moreover, the composition and dopant content of the desiccant, which was used for insulating glass, were investigated to find out the corrosion effect on insulating glass. On the basis of the experimental results, the doping of calcium chloride into desiccant and the humid environment were the main causes for the corrosion failure of insulating glass. Finally, some reasonable suggestions and solution were also proposed.
Key words: insulating glass desiccant; insulating glass lifespan; corrosive; calcium chloride; humid environment
引言
作为材料和生产工艺均很成熟的玻璃制品，中空玻璃因其较长的使用寿命、优良的保温、隔热和隔音等性能，被建筑工程广泛应用[1, 2]。实际应用过程中，为了提高中空玻璃的使用寿命和性能，通常需要采用能够持续控制低温露点的干燥剂[3-6]。但是，中空玻璃会因使用含有氯化钙的干燥剂而内部腐蚀结碱，最终造成失效，出现起雾、结露等现象，严重的甚至会出现玻璃坠落[7, 8]。为了避免中空玻璃内部腐蚀问题的出现，本文系统研究和分析了其腐蚀成因，并为中空玻璃的腐蚀与防护提出了建议和解决方案。
1. 实验过程
1.1 实验材料及仪器设备
实验材料：本文采用的中空玻璃样品是北方某业主单位提供的发生腐蚀失效的硅酮胶密封槽铝式双道密封建筑（安全）中空玻璃，该中空玻璃采用的铝间隔条，铝间隔条内灌装了中空玻璃用B类干燥剂，又通过第一道丁基热熔密封胶和第二道硅酮密封胶将两片玻璃粘接密封在一起。使用腐蚀失效的中空玻璃的门窗是既有住宅门窗，使用时间为7年左右。其它实验材料包括：铝间隔条试片，中空玻璃用干燥剂，氯化钙（分析纯），去离子水，盐酸溶液（1+3），三乙醇胺溶液（1+2），氢氧化钠溶液（100 g/L），钙试剂羧酸钠盐指示剂，乙二胺四乙酸二钠标准溶液（0.05 mol/L）。
实验设备：针对严重腐蚀的中空玻璃及其中的干燥剂，本文采用了宏观观察、化学成分分析、微观结构表征和腐蚀速率计算等方法进行研究，采用的实验设备主要包括：扫描式电子显微镜-能谱仪(Carl Zeiss SMT AG，德国)，X射线衍射仪(Cu-Ka 射线，35 kV，30 mA，l = 0.15418 nm)，X射线荧光光谱分析(ZSX-100e，日本)，分析天平，搅拌器，烧杯，玻璃棒，容量瓶，移液管，锥形瓶，滤纸。
山东省威海银滩中房蔚然海岸小区-含有氯化钙干燥剂对中空玻璃的腐蚀实拍